Description:
The panel comprises a polyethylene core between two aluminum skins, the thickness of LDPE core and two aluminum skin and the width of panel can be designed according to customers requirement, the front surface could be coated with Polyester and PVDF paints or treated of PET film, the protective film which is on the top surface can be peeled off. The back aluminum skin is done by anti-corrosive pretreatment or coated with anti-corrosive paints.
Specifications:
| Alu. Thickness: |
0.1mm, 0.15mm, 0.2mm, 0.25mm, 0.3mm, 0.35mm, 0.4mm, 0.45mm, 0.5mm |
| Panel Thickness: |
2mm, 3mm, 4mm, 5mm, 6mm |
| Width Available: |
1220mm, 1250mm, 1270mm, 1500mm, 1575mm |
| Length Available: |
2440mm, 2800mm, 3200mm, 5000mm, 5850mm |
Tolerance:
| Thickness: |
± 0.2mm |
| Alu. Thickness: |
± 0.02mm |
| Width: |
± 2.0mm |
| Length: |
± 4.0mm |
| Diagonal: |
± 5.0mm |
| Bow: |
Max 0.7% ( 5mm/m ) of the length / width |
Property:
| Paint Thickness (Micron): |
26 ± 2, 18 ± 2 |
| Pencil Hardness: |
2H |
| Toughness Of Coating: |
2T |
| Temperature Resistance: |
-50℃ to +90℃ |
| Impact Strength (kg/cm2): |
50 |
| Boiling Water Resistance: |
Boiling for 2 hours without change |
| Acid Resistance: |
Immerse surface in 2% HC1 for 24hrs without change |
| Alkaline Resistance: |
Immersed surface in 2% NaOH for 24hrs without change |
| Oil Resistance: |
Immerse surface in 20# engine oil for 24hrs without change |
| Solvent Resistance: |
Cleaned 100 times with dimethylbenzene without change |
| Cleaning Resistance: |
>1000 times without change |
| Thermal Expansion: |
2.4mm/m @100℃ temperature difference |
| Peel Strength: |
Average 130 N.mm/mm |
| Bending Strength: |
≧100MPA |
| Bending Elastic Modules: |
≧2.0x104MPA |
| Heat Distortion Temperature: |
≧95℃ |
Granite & Wood 
Aluminum Composite Panel